• Conforms to ASTM B241, EN 754-2, GB/T 6893
• Composition: 99.6% Al min. (Fe+Si ≤0.4%)

 

 

• Tensile Strength: 65–95 MPa
• Yield Strength: 25–55 MPa
• Hardness: 23–32 HV (Hard purity characteristic)

 

 

Tempers: O (annealed), H112 (as-fabricated)
Optimal choice: O temper (superior formability)

 

 

• Size range: OD 10–200 mm × Wall thickness 1–25 mm
• Services: Cut-to-length, bevelling, threading

 

 

• Excellent atmospheric/chemical corrosion resistance
• Natural oxide layer protection (does not require surface treatment)

 

 

• High formability – Ideal for bending/flaring
• Excellent weldability (TIG/MIG recommended)

 

 

• Electrical: 61% IACS (Superior conductivity)
• Thermal: 234 W/m·K
• Primary use: Heat exchangers/busbars

 

 

• Smooth extruded finish (Ra ≤1.6 µm)
• No die lines/seam marks (seamless advantage)

 

 

• MTC with traceable heat numbers
• Third-party reports: SGS, EN 10204 3.1

 

 

• HVAC systems • Electrical conduits • Food processing tubing
• Chemical transport • Decorative structures

 

 

• Low MOQ: 50 kg • Prototypes supported

 

 

• Eddy current tested • Zero weld defects (seamless construction)

 

 

• Straightness: ≤1.5 mm/m
• Tolerance: OD ±0.1mm / WT ±10%

 

 

• 100% recyclable • REACH/ROHS compliant

 

 

• PVC end caps + VCI coating + wooden crate
• Anti-impact corners for long pipes

 

 

Feature	1060 Seamless	Welded Pipe
Corrosion Res.	★★★★★ (Uniform)	★★★☆☆ (Weld zone)
Pressure Rating	25% higher	Baseline

 

 

• SWA Forging certified to ISO 9001 & PED 2014/68/EU
• Full traceability from billet to final pipe

 

 

• Custom diameters/wall thicknesses
• Annealing/aging treatments • Hydrostatic testing